Product Description
UL 40028CC is a copolymer of ethylene and vinyl acetate.
Resin Properties | Typical Value | (English) | Typical Value | (SI) | Test Based On |
Density | 0.948 | g/cm³ | 0.948 | g/cm³ | ASTM D1505 |
Melt Index 2 (190°C/2.16 kg) | 400 | g/10 min | 400 | g/10 min | ASTM D1238 |
Vinyl Acetate Content | 28.0 | wt% | 28.0 | wt% | ExxonMobil Method |
Peak Melting Temperature | 153 | °F | 67 | °C | ExxonMobil Method |
Molded Properties | Typical Value | (English) | Typical Value | (SI) | Test Based On |
Tensile Modulus (0.20 in/min (5.0 mm/min)) | 1600 | psi | 11 | MPa | ASTM D638 |
Tensile Strength at Break | ASTM D638 | ||||
20 in/min (500 mm/min) | 350 | psi | 2.4 | MPa | |
Elongation at Break
(20 in/min (500 mm/min)) |
580 | % | 580 | % | ASTM D638 |
Durometer Hardness (Shore A) | 73 | 73 | ASTM D2240 |
Specification: EVA-26% TO 40%-ExxonMobil-40028CC
|