EVA-18% TO 25%-HANWHA-1316
Product Description
HANWHA EVA 1316 is manufactured by Dow autoclave high pressure process and designed for variety of foam molding application such as shoes and sandals etc. EVA 1316 is well known for its excellent processability and high quality assurance.
| Physical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Density | 0.940 g/cm³ | 0.940 g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.8 g/10 min | 1.8 g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 19.0 wt% | 19.0 wt% | Internal Method |
| Mechanical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Tensile Strength (Break) | 1920 psi | 13.2 MPa | ASTM D638 |
| Tensile Elongation (Break) | 850 % | 850 % | ASTM D638 |
| Hardness | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Durometer Hardness
Shore A |
90 |
90 |
ASTM D2240 |
| Shore D | 36 | 36 | |
| Thermal | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Brittleness Temperature | < -105 °F | < -76.0 °C | ASTM D746 |
| Vicat Softening Temperature | 138 °F | 59.0 °C | ASTM D1525 |
| Peak Melting Temperature | 185 °F | 85.0 °C | ASTM D3417 |
Specification: EVA-18% TO 25%-HANWHA-1316
|