Description
Luban HP3107K is manufactured using the Spheripol Technology. Luban HP3107K is a homopolymer polypropylene designed for the production of biaxially oriented polypropylene films (BOPP). The product is suitable for metallizable film, both as monolayer and in coextruded structures.
Application
Core layer in BOPP film. Packaging bags for food and non-food, plain and laminated garment bags, plain and pigmented label film, lamination film, plain overwrap film, plain and colored adhesive tapes.
Properties (Typical Values)
| Property | Units | Test method | Value |
| Melt flow rate (230°C/2.16 kg) | g/10 min | ISO 1133 | 3.0 |
| Density | g /cm³ | ISO 1183 | 0.90 |
| Tensile modulus (1 mm/min) | MPa | ISO 527-2 | 1450 |
| Tensile stress at yield (50 mm/min) | MPa | ISO 527-2 | 34 |
| Tensile strain at yield (50 mm/min) | % | ISO 527-2 | 9 |
| Tensile strain at break (50 mm/min) | % | ISO 527-2 | > 50 |
| Charpy notched impact strength | kJ/m² | ISO 179/1eA | 4 |
| Heat Deflection Temperature (0.45 MPa) | °C | ISO 75-2 | 85 |
| Vicat Softening Temperature | °C | ISO 306 | 154 |
Specification: BOPP-LUBAN-HP3107K
|