DESCRIPTION
Borstar®FB1200 is produced using the proprietary Borstar® bimodal technology resulting in easy extrusion with superior mechanical properties. Film made from the product exhibits excellent mechanical strength at normal as well as low temperature, good sealing properties and superior ESCR. Borstar®FB1200 contains antioxidant.
| Property | Typical Value* | Test Method |
| Density | 921 kg/m3 | ASTM D 792 |
| Melt Flow Rate (190°C/2.16kg) | 0.17 g/10min | ASTM D1238 |
| Melt Flow Rate (190°C/5.0kg) | 0.70 g/10min | ASTM D1238 |
| Melt Flow Rate (190°C/21.6kg) | 16 g/10min | ASTM D1238 |
| Melting Temperature | 123 °C | ISO 11357/03 |
| Vicat Softening Point A50 (10 N) | 100 °C | ISO 306 |
| ESCR – 10% Igepal – F 50% | >5000 Hours | ASTM D1693-B |
| FILM PROPERTIES¹ | ||
|
Property** |
Typical Value* |
Test Method |
| Tensile Strength at Break (MD/TD) | 62/49 MPa | ISO 527-3 |
| Elongation at Break (MD/TD) | 600/770 % | ISO 527-3 |
| Tensile Strength at Yield (TD) | 12 MPa | ISO 527-3 |
| Tensile Modulus (1 % Secant) (MD/TD) | 250/300 MPa | ASTM D 882 |
| Coefficient of Friction | 0.4 | ASTM D 1894 |
| Gloss (60°) | 10 | ASTM D 2457 |
| Dart Drop | 1200 g | ASTM D 1709/A |
| Tear Strength (MD/TD) | 4/9 N | ASTM D 1922 |
| Puncture Resistance, force | 50 N | ASTM D 5748 |
| Puncture Resistance, energy | 3.0 J | ASTM D 5748 |
Specification: LL HEAVY-BOROUGE-FB1200
|