Product Description
Appliocations:
Paper and paperboard (release paper, kraft paper)
Flexible package( tie layer or sealant layer of laminating film)
Description:
LUTENE LB7000 is mainly intended for extrusion coating and can be processed at high speed with uniform thickness and width. LUTENE LB7000 has a good adhesion strength with paper, paper board and other substrates and excellent neck-in characteristic. LUTENE LB7000 contains no additives.
Physical | Nominal Value Unit | Test Method |
Density | 0.917 g/cm³ | ASTM D1505 |
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 g/10 min | ASTM D1238 |
Mechanical | Nominal Value Unit | Test Method |
Tensile Strength 2
Yield |
8.80 MPa |
ASTM D638 |
Break | 11.8 MPa | |
Tensile Elongation 2 (Break) | 500 % | ASTM D638 |
Flexural Modulus 3 | 177 MPa | ASTM D790 |
Films | Nominal Value Unit | Test Method |
Minimum Heat Seal Temperature
Kraft Paper 40g/m² |
110 |
Internal Method |
Hardness | Nominal Value Unit | Test Method |
Durometer Hardness (Shore D) | 43 | ASTM D2240 |
Thermal | Nominal Value Unit | Test Method |
Vicat Softening Temperature | 83.0 °C | ASTM D1525 4 |
Melting Temperature | 106 °C | DSC |
Extrusion | Nominal Value Unit | Test Method |
Melt Temperature | 280 to 330 °C | |
Minimum Coating Weight
Coating Speed: 150m/min |
13 g/m² |
Internal Method |
Neck-in (Coating Speed: 150m/min) | 20.0 mm | Internal Method |
Specification: LD LAMINATION-LG-LB7500N
|