Features
- Low flow
- Low water carry-over during the extrusion process
- Suitable for the injection moulding of technical articles requiring good mechanical strength
Applications
Extrusion
- Woven industrial fabric for high strength products
- Flexible intermediate bulk containers (FIBC’s)
- Carpet backing
- Sacks and bags
- Monofilaments
- Packaging strapping
| Typical properties (not to be construed as specifications) | Value (SI) | Value (English) | Method | |
| Resin Properties | Melt mass-flow rate – MFR (230/2.16) | 3.5 g/10min | 3.5 g/10min | ISO 1133 |
| Moulding Shrinkage – SMp / SMn | 1.5 / 1.4 % | 1.5 / 1.4 % | ISO 294-4 | |
|
Physical Properties |
Flexural modulus | 1 550 MPa | 224 810 psi | ISO 178 |
| Tensile modulus of elasticity | 1 600 MPa | 232 060 psi | ISO 527-2 | |
| Tensile stress at yield | 34.5 MPa | 5 004 psi | ISO 527-2 | |
| Tensile strain at yield | 9.0 % | 9.0 % | ISO 527-2 | |
| Tensile strain at break | >50 % | >50 % | ISO 527-2 | |
| Charpy notched impact strength (23°C) | 3.5 kJ/m2 | 1.7 ft·lbf/in2 | ISO 179-1 | |
| Ball indentation hardness – HB | 72 N/mm2 | 10 440 psi | ISO 2039-1 | |
|
Thermal Properties |
Melting temperature – DSC | 166°C | 332°F | ISO 11357-3 |
| Heat deflection temperature – HDT / A (1.8 MPa) | 53°C | 127°F | ISO 75-2 | |
| Heat deflection temperature – HDT / B (0.45 MPa) | 85°C | 185°F | ISO 75-2 | |
| Vicat softening temperature – VST / A120 (10 N) | 154°C | 309°F | ISO 306 | |
Specification: PP RAFFIA-SASOL-HKR102
|