| Tensile Modulus – 100% Secant 377
Tensile 1380 |
psi
psi |
2.60
9.50 |
MPa
MPa |
ASTM D638
ASTM D638 |
| Strength 1 (Break, Compression Molded) |
|
|
|
|
|
| Tensile Elongation 1 |
|
|
|
|
ASTM D638 |
| Break, Compression Molded |
810 |
% |
810 |
% |
|
| Flexural Modulus |
|
|
|
|
ASTM D790 |
| 1% Secant : Compression Molded |
2200 |
psi |
15.2 |
MPa |
|
| 2% Secant : Compression Molded |
2090 |
psi |
14.4 |
MPa |
|
| Elastomers |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Tear Strength 2 |
213 |
lbf/in |
37.3 |
kN/m |
ASTM D624 |
| Hardness |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Durometer Hardness |
|
|
|
|
ASTM D2240 |
| Shore A, 1 sec, Compression Molded |
70 |
|
70 |
|
|
| Shore D, 1 sec, Compression Molded |
20 |
|
20 |
|
|
| Thermal |
Nominal Value |
(English) |
Nominal Value |
(SI) |
Test Method |
| Glass Transition Temperature |
-61.6 |
°F |
-52.0 |
°C |
Dow Method |
| Vicat Softening Temperature |
115 |
°F |
46.0 |
°C |
ASTM D1525 |
| Melting Temperature (DSC) 3 |
131 |
°F |
55.0 |
°C |
Dow Method |
| Peak Crystallization Temperature (DSC) |
108 |
°F |
42.0 |
°C |
Dow Method |
There are no reviews yet.