| Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Density | 0.920 | g/cm³ | 0.920 | g/cm³ | ASTM D792 |
| Base Density 1 | 0.920 | g/cm³ | 0.920 | g/cm³ | Dow Method |
| Melt Index (190°C/2.16 kg) | 2.0 | g/10 min | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Film Thickness – Tested | 2 | mil | 51 | µm | |
| Film Puncture Resistance (2.0 mil (51 µm)) | 35.0 | ft·lb/in³ | 2.90 | J/cm³ | Dow Method |
| Film Toughness
MD : 2.0 mil (51 µm) |
1920 |
ft·lb/in³ |
159 |
J/cm³ |
ASTM D882 |
| TD : 2.0 mil (51 µm) | 2230 | ft·lb/in³ | 185 | J/cm³ | |
| Secant Modulus
2% Secant, MD : 2.0 mil (51 µm) |
26200 |
psi |
181 |
MPa |
ASTM D882 |
| 2% Secant, TD : 2.0 mil (51 µm) | 30000 | psi | 207 | MPa | |
| Tensile Strength
MD : Yield, 2.0 mil (51 µm) |
1790 |
psi |
12.3 |
MPa |
ASTM D882 |
| TD : Yield, 2.0 mil (51 µm) | 1760 | psi | 12.1 | MPa | |
| MD : Break, 2.0 mil (51 µm) | 3600 | psi | 24.8 | MPa | |
| TD : Break, 2.0 mil (51 µm) | 3330 | psi | 23.0 | MPa | |
| Tensile Elongation
MD : Break, 2.0 mil (51 µm) |
420 |
% |
420 |
% |
ASTM D882 |
| TD : Break, 2.0 mil (51 µm) | 670 | % | 670 | % | |
| Dart Drop Impact (2.0 mil (51 µm)) | 150 | g | 150 | g | ASTM D1709A |
| Elmendorf Tear Strength 2
MD : 2.0 mil (51 µm) |
500 |
g |
500 |
g |
ASTM D1922 |
| TD : 2.0 mil (51 µm) | 280 | g | 280 | g | |
| Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Vicat Softening Temperature | 209 | °F | 98.3 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 233 | °F | 112 | °C | Dow Method |
| Optical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Gloss (45°, 2.00 mil (50.8 µm)) | 66 | 66 | ASTM D2457 | ||
| Haze (2.00 mil (50.8 µm)) | 7.60 | % | 7.60 | % | ASTM D1003 |
Specification: LD FILM-DOW-690
|