Technical data for PE100 pipe material | ||||
Property | Standard | Unit | PE100 black | |
Specific density at 23°C | ISO 1183 | g/cm3 | 0,95 | |
Melt flow index MFR 190/5 MFR 190/2,16 MFR 230/5
MFI range |
ISO 1133
ISO1872/1873 |
g/10min |
0,30 <0,10
T003 |
|
Mechanical Properties | Tensile stress at yield | ISO 527 | MPa | 25 |
Elongation at yield | ISO 527 | % | 9 | |
Elongation at break | ISO 527 | % | >600 | |
Impact strength unnotched at | ||||
+23°C
Impact strength unnotched at -30°C |
ISO 179 | kJ/m2 | no break
no break |
|
Impact strength notched at | ||||
+23°C
Impact strength notched at 0°C |
ISO 179 | kJ/m2 | 16 | |
Impact strength notched at -30°C | 6 | |||
Ball indentation hardness acc. | ISO 2039-1 | MPa | ||
Rockwell | 46 | |||
Flexural strength (3,5% flexural | ISO 178 | MPa | ||
stress) | 24 | |||
Modulus of elasticity | ISO 527 | MPa | 1100 | |
Resistance to internal pressure | ISO 4427 | No failure or | ||
[20°C, 12.4MPa, 100h] | defect | |||
Resistance to internal pressure | ISO 4427 | No failure or | ||
[80°C, 5.5MPa, 165h] | defect | |||
Resistance to internal pressure | ISO 4427 | No failure or | ||
[80°C, 5.0Pa, 1000h] | defect | |||
Thermal stability OIT 200°C | EN 728 | Min. | > 20min | |
Thermal Properties | Vicat-Softening point VST/B/50 | ISO 306 | °C | 77 |
Heat deflection temperature | ISO 75 | °C | ||
HDT/B | 75 | |||
Linear coefficient of thermal | DIN 53752 | K-1 x 10-4 | ||
expansion | 1,8 | |||
Thermal conductivity at 20 °C | DIN 52612 | W/(mxK) | 0,4 | |
Flammability | UL94 DIN 4102 | — | 94-HB B2 | |
Electrical Properties | Specific
volume resistance |
VDE 0303 | OHM cm | >1016 |
Specific surface resistance | VDE 0303 | OHM | >1013 | |
relative dielectric constant at 1 MHz | DIN 53483 | — | 2,3 | |
Dielectric strength | VDE 0303 | kV/mm | 70 | |
Physiologically non-toxic | EEC 90/128 | — | Yes | |
FDA | — | — | Yes | |
UV stabilized | — | — | carbon black | |
Colour | — | — | black |
Specification: HD PIPE-BASELL-L4904
|