Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Density | 0.924 | g/cm³ | 0.924 | g/cm³ | ASTM D792 |
Base Density 1 | 0.922 | g/cm³ | 0.922 | g/cm³ | Dow Method |
Melt Index (190°C/2.16 kg) | 2.1 | g/10 min | 2.1 | g/10 min | ASTM D1238 |
Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Film Thickness – Tested | 2 | mil | 51 | µm | |
Film Puncture Energy | 12.4 | in·lb | 1.40 | J | Dow Method |
Film Puncture Resistance | 43.5 | ft·lb/in³ | 3.60 | J/cm³ | Dow Method |
Film Toughness
MD |
580 |
ft·lb/in³ |
48.0 |
J/cm³ |
ASTM D882 |
TD | 641 | ft·lb/in³ | 53.0 | J/cm³ | |
Secant Modulus
2% Secant, MD |
25700 |
psi |
177 |
MPa |
ASTM D882 |
2% Secant, TD | 30500 | psi | 210 | MPa | |
Tensile Strength
MD : Yield |
1520 |
psi |
10.5 |
MPa |
ASTM D882 |
TD : Yield | 1530 | psi | 10.5 | MPa | |
MD : Break | 3050 | psi | 21.0 | MPa | |
TD : Break | 2120 | psi | 14.6 | MPa | |
Tensile Elongation
MD : Break |
280 |
% |
280 |
% |
ASTM D882 |
TD : Break | 500 | % | 500 | % | |
Dart Drop Impact | 100 | g | 100 | g | ASTM D1709A |
Elmendorf Tear Strength 2
MD |
460 |
g |
460 |
g |
ASTM D1922 |
TD | 320 | g | 320 | g | |
Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Melting Temperature (DSC) | 228 | °F | 109 | °C | Dow Method |
Optical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
Gloss (45°) | 78 | 78 | ASTM D2457 | ||
Haze | 5.90 | % | 5.90 | % | ASTM D1003 |
Specification: LD FILM-DOW-505I
|