MECHANICAL
Tensile Strength
Break, Die C, 0.125 in, 20 in/min (3.2mm, 500 mm/min) |
1050 psi | 7 MPa | D 412 |
Tensile Elongation
Break, Die C, 0.125 in, 20 in/min (3.2mm, 500 mm/min) |
450.0 % | 450.0 % | D 412 |
Tensile Stress
Die C 0.125 in, 20 in/min (3.2 mm, 500 mm/min) @ 100 % |
375.0 psi | 2.6 MPa | D 412 |
Tear Strength, Die C | 185.0 pli | 32.4 N/mm | D 624 |
Hardness
Shore A, 10 s delay |
65 | 65 | D 2240 |
ELECTRICAL | |||
Volume Resistivity | < 1E3 ohm.cm | < 1E3 ohm.cm | D 257 |
Surface Resistivity | < 1E5 ohm/sq | < 1E5 ohm/sq | D 257 |
Static Decay
MIL-PRF-81705D, 5kV to 50 V, 12% RH |
< 2.00 s |
< 2.00 s |
FTMS101C |
4046.1 | |||
THERMAL | |||
Ignition Resistance* Flammability** | HB @ 1/16 in | HB @ 1.5 mm | D 635 |
PROPERTY NOTES |
Specification: TEO-RTP-ESD C 2800 B-65A PMS
|