Product Description
Low Viscosity, UV stabilized, Mold release improved
Physical | Nominal Value | Unit | Test Method |
Density | 1.20 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 14 | cm³/10min | ISO 1133 |
Molding Shrinkage
Across Flow |
0.50 to 0.70 |
% |
Internal Method |
Flow | 0.50 to 0.70 | % | |
Water Absorption (Saturation, 23°C) | 0.24 | % | ISO 62 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
Tensile Stress (Yield) | 62.0 | MPa | ISO 527-2/50 |
Tensile Strain
Yield |
6.7 |
% |
ISO 527-2/50 |
Break | 120 | % | |
Flexural Modulus 2 | 2300 | MPa | ISO 178 |
Flexural Stress 2 | 93.0 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 67 | kJ/m² | ISO 179 |
Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 | |
Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature
0.45 MPa, Unannealed |
139 |
°C |
ISO 75-2/B |
1.8 MPa, Unannealed | 124 | °C | ISO 75-2/A |
CLTE
Flow |
6.5E-5 |
cm/cm/°C |
ISO 11359-2 |
Transverse | 6.6E-5 | cm/cm/°C |
Specification: PC-MITSUBISHI-3000UR
|