LL METALLOCENE-MARLEX-D139FK
| Nominal Resin Properties | English | SI | Method |
| Melt Index, 190 °C/2.16 kg | — | 1.0 g/10 min | ASTM D1238 |
| Density | — | 0.918 g/cm3 | ASTM D1505 |
| Slip | 1000 ppm | 1000 ppm | — |
| Antiblock | 5000 ppm | 5000 ppm | — |
| Process Aid | Yes | Yes | — |
| Nominal Blown Film Properties @ 1 mil1 | English | SI | Method |
| Haze | 9 % | 9 % | ASTM D1003 |
| Gloss, 60° | 103 | 103 | ASTM D2457 |
| COF | 0.15 | 0.15 | ASTM D1894 |
| Dart | — | 600 g/mil | ASTM D1709 |
| Elmendorf Tear MD/TD | — | 230/440 g/mil | ASTM D1922 |
| Tensile Strength at Yield MD/TD | 1850/1400 psi | 14/10 MPa | ASTM D882 |
| Tensile Strength at Break MD/TD | 8300/6650 psi | 59/49 MPa | ASTM D882 |
| Tensile Elongation at Break MD/TD | 450/560 % | 450/560 % | ASTM D882 |
| 1 % Secant Modulus MD/TD | 24000/27300 psi | 165/188 MPa | ASTM D882 |
| Seal Initiation Temperature2 | 216 °F | 102 °C | ASTM F88 |