Product Description
Exceed™ 1327MA is an ethylene 1-hexene copolymer. Films made from Exceed™ 1327MA have excellent tensile, impact strength, and puncture. These superior strength properties, along with excellent drawability, allow downgauging in bag applications. TnPP is not intentionally added to Exceed™ 1327MA.
| Resin Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Density / Specific Gravity |
0.927 |
g/cm³ |
0.927 |
g/cm³ |
ASTM D792 |
| Melt Index (190°C/2.16 kg) |
1.3 |
g/10 min |
1.3 |
g/10 min |
ASTM D1238 |
| Peak Melting Temperature |
253 |
°F |
123 |
°C |
ExxonMobil Method |
| |
|
|
|
|
|
| Thermal |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Vicat Softening Temperature |
241 |
°F |
116 |
°C |
ExxonMobil Method |
| |
|
|
|
|
|
| Film Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Tensile Strength at Yield MD |
1900 |
psi |
13 |
MPa |
ASTM D882 |
| Tensile Strength at Yield TD |
2100 |
psi |
14 |
MPa |
ASTM D882 |
| Tensile Strength at Break MD |
8300 |
psi |
60 |
MPa |
ASTM D882 |
| Tensile Strength at Break TD |
7300 |
psi |
50 |
MPa |
ASTM D882 |
| Elongation at Break MD |
580 |
% |
580 |
% |
ASTM D882 |
| Elongation at Break TD |
700 |
% |
700 |
% |
ASTM D882 |
| Secant Modulus MD – 1% Secant |
45000 |
psi |
310 |
MPa |
ASTM D882 |
| Secant Modulus TD – 1% Secant |
52000 |
psi |
360 |
MPa |
ASTM D882 |
| Dart Drop Impact |
140 |
g |
140 |
g |
ASTM D1709A |
| Elmendorf Tear Strength MD |
160 |
g |
160 |
g |
ASTM D1922 |
| Elmendorf Tear Strength TD |
430 |
g |
430 |
g |
ASTM D1922 |
| Puncture Force |
11 |
lbf |
48 |
N |
ExxonMobil Method |
| Puncture Energy |
27 |
in·lb |
3.1 |
J |
ExxonMobil Method |
| |
|
|
|
|
|
| Optical Properties |
Typical Value |
(English) |
Typical Value |
(SI) |
Test Based On |
| Gloss (45°) |
16 |
|
16 |
|
ASTM D2457 |
| Haze |
> 30 |
% |
> 30 |
% |
ASTM D1003 |