| Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Density | 0.918 | g/cm³ | 0.918 | g/cm³ | ASTM D792 |
| Base Density 1 | 0.917 | g/cm³ | 0.917 | g/cm³ | Dow Method |
| Melt Index (190°C/2.16 kg) | 1.0 | g/10 min | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Film Thickness – Tested | 1.0 | mil | 25 | µm | |
| Film Puncture Energy | 15.0 | in·lb | 1.69 | J | Dow Method |
| Film Puncture Force | 8.00 | lbf | 35.6 | N | Dow Method |
| Film Puncture Resistance | 110 | ft·lb/in³ | 9.10 | J/cm³ | Dow Method |
| Film Toughness
MD |
850 |
ft·lb/in³ |
70.3 |
J/cm³ |
ASTM D882 |
| TD | 800 | ft·lb/in³ | 66.2 | J/cm³ | |
| Secant Modulus
1% Secant, MD |
26000 |
psi |
179 |
MPa |
ASTM D882 |
| 2% Secant, MD | 23000 | psi | 159 | MPa | |
| 1% Secant, TD | 29000 | psi | 200 | MPa | |
| 2% Secant, TD | 24000 | psi | 165 | MPa | |
| Tensile Strength
MD : Yield |
1700 |
psi |
11.7 |
MPa |
ASTM D882 |
| TD : Yield | 1600 | psi | 11.0 | MPa | |
| MD : Break | 4900 | psi | 33.8 | MPa | |
| TD : Break | 4000 | psi | 27.6 | MPa | |
| Tensile Elongation
MD : Break |
400 |
% |
400 |
% |
ASTM D882 |
| TD : Break | 450 | % | 450 | % | |
| Dart Drop Impact | 450 | g | 450 | g | ASTM D1709A |
| Elmendorf Tear Strength
MD |
250 |
g |
250 |
g |
ASTM D1922 |
| TD | 550 | g | 550 | g | |
| Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Vicat Softening Temperature | 212 | °F | 100 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 253 | °F | 123 | °C | Dow Method |
| Optical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Gloss (45°) | 33 | 33 | ASTM D2457 | ||
| Haze | 22 | % | 22 | % | ASTM D1003 |