| Physical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Density | 0.919 | g/cm³ | 0.919 | g/cm³ | ASTM D792 |
| Base Density | 0.918 | g/cm³ | 0.918 | g/cm³ | Dow Method 1 |
| Melt Index (190°C/2.16 kg) | 1.0 | g/10 min | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Film Thickness – Tested | 2.0 | mil | 51 | µm | |
| Film Puncture Resistance (2.0 mil (51 µm)) | 99.0 | ft·lb/in³ | 8.19 | J/cm³ | Dow Method |
| Secant Modulus
2% Secant, MD: 2.0 mil (51 µm) |
26600 |
psi |
183 |
MPa |
ASTM D882 |
| 2% Secant, TD: 2.0 mil (51 µm) | 31500 | psi | 217 | MPa | |
| Tensile Strength
MD: Yield, 2.0 mil (51 µm) |
1500 |
psi |
10.3 |
MPa |
ASTM D882 |
| TD: Yield, 2.0 mil (51 µm) | 1600 | psi | 11.1 | MPa | |
| MD: Break, 2.0 mil (51 µm) | 4600 | psi | 31.7 | MPa | |
| TD: Break | 3630 | psi | 25.1 | MPa | |
| Tensile Elongation
MD: Break, 2.0 mil (51 µm) |
660 |
% |
660 |
% |
ASTM D882 |
| TD: Break, 2.0 mil (51 µm) | 710 | % | 710 | % | |
| Dart Drop Impact (2.0 mil (51 µm)) | 100 | g | 100 | g | ASTM D1709A |
| Elmendorf Tear Strength
MD: 2.0 mil (51 µm) |
110 |
g |
110 |
g |
ASTM D1922 2 |
| TD: 2.0 mil (51 µm) | 260 | g | 260 | g | |
| Thermal | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Vicat Softening Temperature | 214 | °F | 101 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 241 | °F | 116 | °C | Dow Method |
| Optical | Nominal Value | (English) | Nominal Value | (SI) | Test Method |
| Gloss (20°, 2.00 mil (50.8 µm)) | 69 | 69 | ASTM D2457 | ||
| Haze (2.00 mil (50.8 µm)) | 11 | % | 11 | % | ASTM D1003 |
Specification: LL FILM-DOW-1210P
|