PETLIN LD C150Y is a low density polyethylene resin for general purpose and film applications. It is produced by the state-of-the-art DSM Stamicarbon tubular process. It contains antioxidant (BHT free), slip and antiblock additives. It is intended primarily for blown film process.
| Physical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Density | 0.921 g/cm³ | 0.921 g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 g/10 min | 5.0 g/10 min | ISO 1133 |
| Mechanical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Coefficient of Friction | 0.10 | 0.10 | ASTM D1894 |
| Films | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Film Thickness – Tested | 0.98 mil | 25 µm | |
| Film Thickness – Recommended / Available | 150 to 60 µm | 150 to 60 µm | |
| Tensile Modulus
MD : 0.98 mil (25 µm) |
29300 psi |
202 MPa |
ISO 527-3 |
| TD : 0.98 mil (25 µm) | 32500 psi | 224 MPa | |
| Tensile Stress
MD : Break, 0.98 mil (25 µm) |
3770 psi |
26.0 MPa |
ISO 527-3 |
| TD : Break, 0.98 mil (25 µm) | 2180 psi | 15.0 MPa | |
| Tensile Elongation
MD : Break, 0.98 mil (25 µm) |
150 % |
150 % |
ISO 527-3 |
| TD : Break, 0.98 mil (25 µm) | 610 % | 610 % | |
| Dart Drop Impact (0.98 mil (25 µm)) | 86 g | 86 g | ASTM D1709 |
| Elmendorf Tear Strength
MD : 0.98 mil (25 µm) |
18000 lbf |
80000 N |
ISO 6383-2 |
| TD : 0.98 mil (25 µm) | 6700 lbf | 30000 N | |
| Optical | Nominal Value (English) | Nominal Value (SI) | Test Method |
| Gloss (45°, 0.984 mil (25.0 µm)) | 66 | 66 | ASTM D2457 |
| Haze (0.984 mil (25.0 µm)) | 6.5 % | 6.5 % | ASTM D1003 |
| Extrusion | Nominal Value (English) | Nominal Value (SI) | |
| Melt Temperature | 293 to 329 °F | 145 to 165 °C | |