high strength POM dupont 900P NC010 granuels impact resistance rigidity virgin pom resin

Physical Properties

Metric

English

Comments

Density 

1.42 g/cc

0.0513 lb/in³

ISO 1183

Water Absorption 

1.4 %
@Thickness 2.00 mm

1.4 %
@Thickness 0.0787 in

Sim. to ISO 62

Moisture Absorption 

0.400 %
@Thickness 2.00 mm

0.400 %
@Thickness 0.0787 in

Sim. to ISO 62

Linear Mold Shrinkage, Flow 

0.019 cm/cm

0.019 in/in

ISO 294-4, 2577

Linear Mold Shrinkage, Transverse 

0.019 cm/cm

0.019 in/in

ISO 294-4, 2577

Melt Flow 

21 g/10 min
@Load 2.16 kg,
Temperature 190 °C

21 g/10 min
@Load 4.76 lb,
Temperature 374 °F

cm³/10min Volumetric; ISO 1133

25 g/10 min
@Load 2.16 kg,
Temperature 190 °C

25 g/10 min
@Load 4.76 lb,
Temperature 374 °F

ISO 1133

Mechanical Properties

Metric

English

Comments

Hardness, Rockwell M 

92

92

ISO 2039-2

Hardness, Rockwell R 

120

120

ISO 2039-2

Ball Indentation Hardness 

170 MPa

24700 psi

H 961/30; ISO 2039-1

Tensile Strength, Yield 

71.0 MPa

10300 psi

ISO 527-1/-2

Elongation at Break 

23 %

23 %

Nominal; ISO 527-1/-2

Elongation at Yield 

12 %

12 %

ISO 527-1/-2

Tensile Modulus 

3.20 GPa

464 ksi

ISO 527-1/-2

Flexural Modulus 

3.00 GPa

435 ksi

ISO 178

Poissons Ratio 

0.37

0.37