F5001 is a general purpose extrusion film grade HDPE produced by the Spherilene Technology. This grade is characterized by good processability and mechanical strength.
F5001 can be used as blending resin in HDPE film for packaging application
| Property | Test Method | Unit | Value |
| Melt Flow Index (2.16 kg, 190°C) | ASTM D1238 | g/10 min | 1.1 |
| Density (23°C) | ASTM D1505 | g/cm3 | 0.95 |
| Physical Property | |||
| Tensile Strength at Yield | ASTM D638 | MPa | 23 |
| Tensile Strength at Break | (50 mm/min) | MPa | 35 |
| Tensile Strength at Break | ASTM D 638 | MPa | 35 |
| (50 mm/min) | |||
| Elongation at Break | % | >1000 | |
| Notched Izod Impact Strength (23°C) | ASTM D 256A | J/m | 450 |
| Flexural Modulus | ASTM D 790A | MPa | 1000 |
| Hardness | ASTM D 2240 | Shore D | 61 |
| DSC Melting Temperature | ASTM D 3418 | °C | 131 |
| Suggested Processing Conditions | |||
| Barrel Temperature | °C | 180-220 | |
| BUR | – | 3 – 6 | |