Product Description
HTA 001HD5 is a high molecular weight HDPE film grade. Films made from HTA 001HD5 exhibit excellent impact and toughness properties as well as high stiffness.
General | ||||
Availability 1 | • Africa & Middle East | • Asia Pacific | ||
Additive | • Antiblock: No | • Slip: No | • Thermal Stabilizer: Yes | |
Applications | • Blown Film
• Grocery Sacks • Liners |
• Produce Bags
• Produce Bags On A Roll • Refuse Bags |
• Thin Gauged Consumer Bags
• Trash Can Liners |
|
Revision Date | • 09/15/2016 | |||
Resin Properties | Typical Value | (English) | Typical Value | (SI) Test Based On |
Density | 0.952 | g/cm³ | 0.952 | g/cm³ ASTM D1505 |
High Load Melt Index (190°C/21.6 kg) | 9.0 | g/10 min | 9.0 | g/10 min ASTM D1238 |
Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.32 | g/10 min | 0.32 | g/10 min ASTM D1238 |
Thermal | Typical Value | (English) | Typical Value | (SI) Test Based On |
Vicat Softening Temperature | 259 | °F | 126 | °C ASTM D1525 |
Film Properties | Typical Value | (English) | Typical Value | (SI) Test Based On |
Tensile Strength at Yield MD | 5900 | psi | 41 | MPa ASTM D882 |
Tensile Strength at Yield TD | 4400 | psi | 30 | MPa ASTM D882 |
Tensile Strength at Break MD | 8600 | psi | 60 | MPa ASTM D882 |
Tensile Strength at Break TD | 8100 | psi | 60 | MPa ASTM D882 |
Elongation at Break MD | 220 | % | 220 | % ASTM D882 |
Elongation at Break TD | 430 | % | 430 | % ASTM D882 |
Secant Modulus MD – 1% Secant | 170000 | psi | 1200 | MPa ASTM D882 |
Secant Modulus TD – 1% Secant | 170000 | psi | 1200 | MPa ASTM D882 |
Dart Drop Impact | 190 | g | 190 | g ASTM D1709A |
Elmendorf Tear Strength MD | 8 | g | 8 | g ASTM D1922 |
Elmendorf Tear Strength TD | 30 | g | 30 | g ASTM D1922 |
Specification: HD HM-ExxonMobil-HTA001HD5
|
User Reviews
Be the first to review “HD HM-ExxonMobil-HTA001HD5”
Vendor Information
- Store Name: Natraj
- Vendor: Natraj
-
Address:
A-250, Narela Industrial Area
110040
Delhi - No ratings found yet!
There are no reviews yet.