ExxonMobil™ HD 7960.13 is a high molecular weight high density polyethylene blown film resin. Films made from HD 7960.13 resin exhibit excellent impact and toughness properties, as well as high stiffness. HD 7960.13 resin is particularly recommended for films less than 0.5 mil in thickness.
| Resin Properties | Typical Value | (English) | Typical Value | (SI) Test Based On |
| Density | 0.952 | g/cm³ | 0.952 | g/cm³ ASTM D1505 |
| Melt Index (190°C/2.16 kg) | 0.060 | g/10 min | 0.060 | g/10 min ASTM D1238 |
| High Load Melt Index (190°C/21.6 kg) | 9.3 | g/10 min | 9.3 | g/10 min ASTM D1238 |
| Peak Melting Temperature | 266 | °F | 130 | °C ExxonMobil
Method |
| Film Properties | Typical Value | (English) | Typical Value | (SI) Test Based On |
| Tensile Strength at Yield MD | 5400 | psi | 37 | MPa ASTM D882 |
| Tensile Strength at Yield TD | 4700 | psi | 32 | MPa ASTM D882 |
| Tensile Strength at Break MD | 13000 | psi | 90 | MPa ASTM D882 |
| Tensile Strength at Break TD | 10000 | psi | 70 | MPa ASTM D882 |
| Elongation at Break MD | 290 | % | 290 | % ASTM D882 |
| Elongation at Break TD | 390 | % | 390 | % ASTM D882 |
| Secant Modulus MD – 1% Secant | 150000 | psi | 1000 | MPa ASTM D882 |
| Secant Modulus TD – 1% Secant | 160000 | psi | 1100 | MPa ASTM D882 |
| Dart Drop Impact | 320 | g | 320 | g ASTM D1709A |
| Elmendorf Tear Strength MD | 7 | g | 7 | g ASTM D1922 |
| Elmendorf Tear Strength TD | 40 | g | 40 | g ASTM D1922 |
Specification: HD HM-ExxonMobil-7960.13
|
User Reviews
Be the first to review “HD HM-ExxonMobil-7960.13”
Vendor Information
- Store Name: Natraj
- Vendor: Natraj
-
Address:
A-250, Narela Industrial Area
110040
Delhi - No ratings found yet!
There are no reviews yet.