DESCRIPTION
Borstar®FB5600 is produced using the proprietary Borstar® bimodal technology resulting in easy extrusion with superior mechanical properties. Product offers excellent balance of stiffness, barrier properties and good processability for multilayer blown film structures.
Borstar®FB5600 when used in combination with Borstar®PE / LDPE / PP products for multilayer films, it offers excellent stiffness and barrier properties.
| PHYSICAL PROPERTIES |
|
| Property |
Typical Value* |
Test Method |
| Density |
960 kg/m3 |
ASTM D 792 |
| Melt Flow Rate (190°C/2.16kg) |
0.7 g/10min |
ASTM D1238 |
| Melt Flow Rate (190°C/21.6kg) |
42 g/10min |
ASTM D1238 |
| Melting Temperature |
132 °C |
ISO 11357/03 |
| Vicat Softening Point A50 (10 N) |
127 °C |
ISO 306 |
| ESCR – 10% Igepal – F 50% |
>72 Hours |
ASTM D1693-B |
FILM PROPERTIE
| Property** |
Typical Value* |
Test Method |
| Tensile Strength at Break (MD/TD) |
74/32 MPa |
ISO 527-3 |
| Elongation at Break (MD/TD) |
500/5 % |
ISO 527-3 |
| Tensile Strength at Yield (MD/TD) |
32/33 MPa |
ISO 527-3 |
| Tensile Modulus (1 % Secant) (MD/TD) |
1100/1650 MPa |
ASTM D 882 |
| Elmendorf tear strength (MD/TD) |
12/800 g |
ASTM D 1922 |
| Dart Drop |
<40 g |
ASTM D 1709/A |
| Puncture Resistance, force |
30 N |
ASTM D 5748 |
| Puncture Resistance, energy |
0.7 J |
ASTM D 5748 |