| Nominal Physical Properties(1) |
English |
SI |
Method |
| Density |
— |
0.953 g/cm3 |
ASTM D1505 |
| Melt Index, 190 °C/2.16 kg |
— |
6.6 g/10 min |
ASTM D1238 |
| Tensile Strength at Yield, 2 in/min, Type IV bar |
4,100 psi |
28 MPa |
ASTM D638 |
| Elongation at Break, 2 in/min, Type IV bar |
950 % |
950 % |
ASTM D638 |
| Flexural Modulus, Tangent – 16:1 span:depth, 0.5 in/min |
185,000 psi |
1,270 MPa |
ASTM D790 |
| ESCR, Condition B (100 % Igepal), F50 |
20 h |
20 h |
ASTM D1693 |
| Durometer Hardness, Type D (Shore D) |
62 |
62 |
ASTM D2240 |
| Vicat Softening Temperature, Loading 1, Rate A |
257 °F |
125 °C |
ASTM D1525 |
| Brittleness Temperature, Type A, Type I specimen |
< -103 °F |
< -75 °C |
ASTM D746 |
There are no reviews yet.