Greenflex FL 55 is an ethylene vinyl acetate copolymer (EVA) for extrusion/co-extrusion blown and cast film.
Films produced with Greenflex FL 55 show a low fish eyes content, high elasticity, good optical properties, good sealability at low temperatures.
Greenflex FL 55 is recommended for the production of co-extrusion film, lamination film, stretch film, barrier film for food packaging and all those aplications where the typical purity of film grades is required.
Main Properties | |||
Resin Properties | Value | Unit | Test Method |
Melt Flow Rate (190 °C/2.16 kg) | 2.5 | g/10min | ISO 1133 |
Vinyl acetate content | 19 | % | Internal method |
Density | 0.941 | g/cm3 | ISO 1183 |
Melting Point | 85 | °C | Internal method |
Brittleness temperature | <- 80 | °C | ASTM D 746 |
Vicat softening point (1 kg) | 58 | °C | ISO 306/A |
Film Properties * |
Value |
Unit |
Test Method |
Tensile stress at yield MD | 4.5 | MPa | ISO 527-3 |
Tensile stress at yield TD | 4 | MPa | ISO 527-3 |
Tensile stress at break MD | 30 | MPa | ISO 527-3 |
Tensile stress at break TD | 27 | MPa | ISO 527-3 |
Elongation at break MD | 560 | % | ISO 527-3 |
Elongation at break TD | 750 | % | ISO 527-3 |
1% Secant modulus MD | 45 | MPa | ISO 527-3 |
1% Secant modulus TD | 53 | MPa | ISO 527-3 |
Elmendorf tear resistance MD | 20 | N/mm | ISO 6383-2 |
Elmendorf tear resistance TD | 50 | N/mm | ISO 6383-2 |
Impact resistance F50 (Dart Drop Test) | 420 | g | ISO 7765-1/A |
Dynamic coefficient of friction (COF) | > 0.5 | – | ISO 8295 |
Haze | 1.5 | % | ISO 14782 |
Gloss, 45° | 85 | % | ASTM D 2457 |
Recommended film thickness | 25 ÷ 80 | micron | – |
Mechanical Properties ** | Value | Unit | Test Method |
ShoreA: | 89 | Shore A | ISO 868 A |
ShoreD: | 36 | Shore D | ISO 868 A |
Specification: EVA-18% TO 25%-GREENFLEX-FL55
|