Description
Luban polypropylene is manufactured using Novolen vertical stirred Gas-phase polymerization process. Luban HP3104K is a homopolymer polypropylene, it is suitable for high speed metallisable Biaxially Oriented Polypropylene (BOPP) film.
Application
Core layer in BOPP film. Food and non-food packaging bags, plain and laminated garment bags, plain and pigmented label film, lamination film, plain overwrap film, plain and colored adhesive tapes.
Properties (Typical Values)
| Property | Units | Test method | Value |
| Melt flow rate (230°C/2.16 kg) | g/10 min | ISO 1133 | 3.3 |
| Density | g /cm³ | ISO 1183 | 0.90 |
| Tensile modulus (1 mm/min) | MPa | ISO 527-2 | 1450 |
| Tensile stress at yield (50 mm/min) | MPa | ISO 527-2 | 34 |
| Tensile strain at yield (50 mm/min) | % | ISO 527-2 | 9 |
| Tensile strain at break (50 mm/min) | % | ISO 527-2 | > 50 |
| Charpy unnotched impact strength | kJ/m² | ISO 179/1eU | 190 |
| Charpy notched impact strength (+23°C) | kJ/m² | ISO 179/1eA | 4 |
| Heat Deflection Temperature (0.45 MPa) | °C | ISO 75-2 | 85 |
Specification: BOPP-LUBAN-HP3104K
|