73005TU is a LLDPE Roto Molding Grade produced by the Spherilene Technology with controlled morphology, excellent balance of processability, mechanical properties & UV stability
This grade is stabilized adequately with Light Stabilizer + to give a long service life under outdoor exposure 73005TU is ideally suited for Tanks & Containers with good UV stability for domestic & industrial water storage, sanitation & agriculture BIS Designation Code: IS 7328-2B-RDO-CDC |
|||
Property | Test Method | Unit | Value |
Melt Flow Index (2.16 kg, 190°C) | ASTM D1238,
IS 13360 (Part 4/Sec 1) |
g/10 min |
5.0 |
Melt Flow Index (5 kg, 190°C) | 14 | ||
Melt Flow Index (21.6 kg, 190°C) | ASTM D1238 | g/10 min | 120 |
Density (23°C) | ASTM D1505,
IS 13360 (Part 3/Sec 11) |
g/cm3 | 0.934 |
Density (23°C) | IS 2530 | g/cm3 | 0.932 – 0.936 |
Physical Property | |||
Tensile Strength at Yield | ASTM D638
(50 mm/min) |
MPa | 17 |
Elongation at Break | % | 500 | |
Notched Izod Impact Strength (23°C) | ASTM D256A | J/m | 350 |
Flexural Modulus | ASTM D790A | MPa | 450 |
Heat Deflection Temperature (0.455 MPa) | ASTM D648 | °C | 74 |
Vicat Softening Point (10 N) | ASTM D1525 | °C | 111 |
DSC Melting Temperature | ASTM D3418 | °C | 126 |
ESCR (F50, 10% Igepal soln. v/v) | ASTM D1693B | Hr | 100 |
Suggested Processing Conditions | |||
Oven Temperature | 240 – 280 °C |
Specification: LL ROTO-HALDIA-73005TU
|